ZT11A-H4F
2018-12-25 1496
产品型号 | ZT11A-H4F | 颜色 | 本色 |
测试项目 | 检测标准 | 单位 | 数据 |
密度 | ISO 1183 | g/cm3 | 1.05 |
拉伸强度 | ISO 527 | MPa | 25 |
断裂伸长率 Elongation at Break | ISO 527 | % | 50 |
弯曲强度 | ISO 178 | MPa | 32 |
弯曲模量 | ISO 178 | MPa | 2100 |
IZOD缺口冲击强度 IZOD Notched Impact Strength | ISO 180 | kJ/㎡ | 7.5 |
-20℃/6H缺口冲击强度 -20℃/6H Notched Impact Strength | ISO 180 | kJ/㎡ | -- |
热变形温度 | ISO 75 | ℃ | 120 |
熔融指数 | ISO 1133 | g/10min | 19.6 |
备注： 以上数据为实验典型值,仅供参考,不作质保承诺.
-